Your present location:首页ProductsHot Work Tool SteelH21,1.2581,SKD5 - H21/1.2581/SKD5 Hot Work Tool Steel bar/plate/forgings/sheet for cutting/mold
产品中心
  • Product Name: H21/1.2581/SKD5 Hot Work Tool Steel bar/plate/forgings/sheet for cutting/mold
  • Product ID: 1402
  • 上架时间: 2017-09-05
  • Views : 745

Favorite Friends Recommend

Chemical Composition%

Standard

Steel Grade

C

Si

Mn

P

S

Cr

Mo

V

W

DIN

1.2581

0.25-0.35

0.15-0.30

0.20-0.40

0.035

0.035

2.50-2.80

-

0.30-0.40

8.00-9.00

ASTM

H21

0.26-0.36

0.15-0.50

0.15-0.40

0.030

0.030

3.00-3.75

-

0.30-0.60

8.50-10.0

GB

3Cr2W8V

0.30-0.40

≤0.40

≤0.40

0.030

0.030

2.20-2.70

-

0.20-0.50

7.50-9.00

Specification

Round bar

Diameter

Length

-

Forged round bar:φ50~250

2000~6000

-

 Rolled round barφ10~65

 2000~6000

-

Flat bar

Thickness(mm)

Width(mm)

Length(mm)

Forged plate20~200

50~710

2000~6000

Rolled plate10~65

155~610

2000~6000

 

Characteristics

1.High intensity and hardness under at high temperature. Hardness can reach 300HBS at 650℃.

2.Fault surface within 80mm in thickness can be fully hardened.

3.Relatively high phrase transformation temperature good hot fatigue resistance to alternation of heat and cold.

4.Plasticity and toughness are comparatively low.

 

Application

1.For making mould which is working at high temperature and stress but without impact load.

2.For making mould which can afford high compressive stress, bending stress and tensile stress.

3.For making metal parting tool which is working under high temperature.

 

Delivery condition

Annealed, hardness is below 255HB.

 

Heat Treatment      

Soft Annealing(℃)

Cooling

Hardness(HB)

Hardening()

In

Hardness(HRC)

740-780

Furnace

Max.241

1050-1100

Oil

49-52 HRC

660-680

Air

 

 Quenching Technique

Quenching Temperature

  Cooling

Hardness HRC

Medium

Temperature

Continuation

Cooling till reaching 20℃

1050-1100

 

Oil

20-60

  Last to 150-180℃

Air

49-52

 

Forging Technique

Heat temperature

 

Initial Forging Temperature

Finish Forging Temperature

Cooling

1130-1160

 

1080-1120

900-850

air cooling then burial pit or sand cooling

 

 Tempering process

Tempering process

Heating Temperature

Medium

Hardness HRC

Elimination stress, stabilize structure&dimension

600-620

  Air

48-52

There is no corresponding message.

  To be closed automatically in X seconds

View my favorites

 
Content:
* Entered characters:0 Word
Less than or equal500
Your e-mail:
 
Example: example@mail.com
Cellphone number:
 
By digital ,"+", in the bars "-" the composition, the maximum allowable 20 characters
Telephone:
 
Less than or equal to 32 characters (including 0-9, -, (,), comma)
Company name:
 
Address:
 
Verification code: